Products	Zinc Chrome Metal
Color
Usage Features	Single pack, modified alkyd based, air drying solvent based anti-corrosive primer with Zinc chrome content. Compatible with NC, Stoving & PU coatings.
Mixing Ratio	Dilute with 30% of Enamel or NC Thinner V-13 x
Application Method	By Spray / Brush
No of Coats	1 - 2 coats
Pot Life	Not Applicable
Drying Time	20 mins / 8 hours
Flash Off	10 - 15 mins
Sand Paper	P-180 / P-240
Method of Sanding	Dry Sanding
Background	Not Required
Hardener/Induction Period	Bare M.S. metal thoroughly cleaned from rust, grease etc., and scrub with 100 no emery paper.
Buffing	70 ± 5 sec / 4 cup
Supply Viscosity	120 ± 5 sec / 4 cup
Spray Viscosity	Not Applicable
Theoretical Coverage	110 - 120 sq.ft

 

 

Products	Speed Kote Primer Surfaces
Color
Usage Features	A versatile single pack, Hi-build, air drying primer surface having good adhesion to Oil & Etch primers. Compatible with NC, Stoving & PU coatings.
Mixing Ratio	Dilute with 30% of Enamel or NC Thinner V-13 x
Application Method	By Spray / Brush
No of Coats	2 - 3 coats
Pot Life	Not Applicable
Drying Time	20 mins /8 hours
Flash Off	10 - 15 mins
Sand Paper	P-240 / P.320
Method of Sanding	Wet or Dry
Background	Anti-corrosive primer applied and scrubbed surface
Hardener/Induction Period	Not Applicable
Buffing	Not Required
Supply Viscosity	130 ± 5 sec / 4 cup
Spray Viscosity	22 ± 2 sec / 4 cup

 

 

Products	NC Putty- Grey
Color
Usage Features	Fast drying, NC based Hi-solid filler to seal micro dents and yields better adhesion to Surfaces. Highly suitable for Industrial purpose.
Mixing Ratio	Dilute with NC Thinner as required
Application Method	By Putty knife
No of Coats	As required
Pot Life	Not Applicable
Drying Time	4 hours
Flash Off	10 - 15 mins
Sand Paper	P- 50 / P- 80
Method of Sanding	Wet Sanding
Background	Oil / NC / PU base surface primer applied and scrubbed panels
Hardener/Induction Period	Not Applicable
Buffing	Not Required
Supply Viscosity	Semi - Solid
Spray Viscosity	Not Applicable
Theoretical Coverage	Flash Point above 20° deg C

 

 

Products	Synthetic Enamel
Usage Features	long oil alkyd resin based enamel has better outdoor exposure on all types of metal and Auto body. Recommended for economical auto refinish due to its excellent gloss level.
Mixing Ratio	Dilute with 30% of Enamel or NC Thinner V-13 x
Application Method	By Spray
No of Coats	1 Coat
Pot Life	Not Applicable
Drying Time	3-4 hrs / 24 hours
Sand Paper	P-400 / P-600
Method of Sanding	Dry or wet Sanding
Background	Well scrubbed Speed kote surface primer applied area
Hardener/Induction Period	Not Applicable
Buffing	Not Required
Supply Viscosity	120 ± 5 sec/4 cup
Spray Viscosity	20 ± 2 sec/4 cup
Theoretical Coverage	120- 130 sq.ft
Flash Point	Above 27° deg C

 

 

 

Products	Synthetic Fast Drying Aluminum
Usage Features	Single pack, Heat (up to 225 deg C) & Corrosion resistant metal coating has very fast air drying mechanism. Both flat and sparkle finishes are available.
Mixing Ratio	Dilute with 30% of Mathulac Thinner Sk - 58.
Application Method	By Spray
No of Coats	1 Coat
Pot Life	Not Applicable
Drying Time	10 mins / 24 hours
Flash Off	10r- 15 mins
Sand Paper	-
Method of Sanding	-
Background	Well scrubbed Speed kote primer surface applied area.
Hardener/lnduction Period	Not Applicable
Buffing	Not Required
Supply Viscosity	80 ± 5sec/4cup
Spray Viscosity	22 ± 2 sec / 4 cup
Theoretical Coverage	100 - 110 sq.ft
Flash Point	Above 27° deg C

 

 

Products	Synthetic Enamel Clear
Usage Features	Long oil alkyd resin based enamel has better outdoor exposure Top coat clear for Industrial / Auto refinish sector.
Mixing Ratio	Dilute with 30% of Enamel or NC Thinner V-13 x
Application Method	By Spray
No of Coats	1 Coat
Pot Life	Not Applicable
Drying Time	3-4 hrs / 24 hours
Sand Paper	P-400 / P-600
Method of Sanding	Dry or wet Sanding
Background	Synthetic based  Solid color applied smooth surface.
Hardener/Induction Period	Not Applicable
Buffing	Not Required
Supply Viscosity	120 ± 5 sec/4 cup
Spray Viscosity	20 ± 2 sec/4 cup
Theoretical Coverage	120 - 130 sq.ft
Flash Point	Above 27° deg C